Physicothermal and topography analysis of polyurethane modified bitumen with rediset for WMA application

The effects of modifying a 60/70 penetration grade bitumen with 3 wt% polyurethane (PU) and a Warm Mix Asphait (WMA) additive namely Rediset, were explored in this research. The penetration, softening point, viscosity, and ductility tests were employed for consistency testing, while the Differential Scanning Calorimetry was used for thermal characterisation. The topography and surface roughness of the modified bitumen were evaluated using Atomic Force Microscopy. Adding PU and Rediset to the base bitumen (BB) stiffens the BB slightly, giving It a lower penetration and higher viscosity values, which Improves the rutting resistance. The thermal transition of the glass temperature and melting temperature are similar to the BB. Furthermore, the addition of PU and Rediset into BB shows a ciear bee structure topography in dry condition indicating better dispersion while in wet condition, the bee structure is mostly affected in the catana and para phase that reveals a reduced in the the wax content of the BB. The bitumen modified with PU and Rediset has a lower surface roughness than BB, making it less susceptible to moisture damage.